Influence of Sintering Temperature on Pore Structure and Apatite Formation of a Sol–Gel-Derived Bioactive Glass

Published on January 25th, 2010 | By: Eileen De Guire

Volume 93 Issue 1, Pages 32 – 35

Bo Lei, Xiaofeng Chen, Yingjun Wang, Naru Zhao, Chang Du, Liming Fang
Published Online: Oct 29 2009 6:04PM
DOI: 10.1111/j.1551-2916.2009.03358.x

 

ABSTRACT
Content, content, content

The aim of this work was to investigate the influence of sintering temperature on the porous morphology, pore-size distribution, and apatite formation of sol-gel-derived porous bioactive glasses. For this purpose, three porous bioactive glasses were prepared by thermal phase separation cotemplate method in sol-gel process followed by sintering at 600°, 800°, and 1000°C. Pore structure of samples was characterized by various methods. The in vitro apatite formation test was carried out in simulated body fluid. The results showed that sintered bioactive glasses at 600°C exhibited a bimodal pore size distribution, mesopores, and nanopores (8-100 nm), macropores (100 nm-1 μm), and nanoscale pore walls (about 100 nm in width). The increase of sintering temperature induced the presence of a submicrometer pore-size distribution (300 nm-3 μm) with nanoscale pore walls (about 200 nm in width) and a morphological transformation from particle-like pore walls to dense pore walls. Depending on this porous structure, as-synthesized samples exhibited faster apatite formation capability.

 

Online Access to Journal of the American Ceramic Society


Back to Previous Page
« « Previous Post     |    Next Post » »





Comments are closed.

Back to Top ↑