Luminescence and Site Symmetry Studies of New Red Phosphors (Ca, Ba)3(VO4)2:Eu3+ Under Blue Excitation

Published on January 26th, 2010 | By: pwray@ceramics.org

Volume 93 Issue 1, Pages 138 – 141

Han-Yu Lin, Ying-Chien Fang, Xiao-Rong Huang, Sheng-Yuan Chu
Published Online: Oct 6 2009 11:47AM
DOI: 10.1111/j.1551-2916.2009.03338.x

ABSTRACT
In this paper, the (Ca, Ba)3(VO4)2:Eu3+ red phosphors were prepared by the solid-state reaction method for the first time, and the preferable sintered condition was obtained at 1050°C for 6 h. To improve the luminescence intensity of Ca2.82(VO4)2:0.12Eu3+, an attempt was made to replace Ca2+ by Ba2+. It was found that the substitution of 6.7%-9.9% Ba2+ ions instead of the Ca2+ ions enhanced the emission intensity under 465 nm excitation. According to the changes of the lattice constants, this enhancement can originate from the lower site symmetry of the Eu3+ ion in the center with noninversion symmetry. And we observed the optimum value of the Ba2+ content (y) was at 9.9 mol% in (Ca1-yBay)2.82(VO4)2:0.12Eu3+. Compared with commercial oxysulfide and sulfide red phosphors suitable for blue excitation, our synthesized phosphor (Ca, Ba)3(VO4)2:Eu3+ has the advantages of no chemical instability or sulfur pollution. In addition, the emission peak at 614 nm and the CIE (International Commission on Illumination) chromaticity points of (0.644, 0.355) for the (Ca0.901Ba0.099)2.82(VO4)2:0.12Eu3+ phosphor indicate this phosphor can be used as a potential candidate for the phosphor-converted white light emitting diode with a blue chip (450-470 nm).

Online Access to Journal of the American Ceramic Society


Back to Previous Page
« « Previous Post     |    Next Post » »





Comments are closed.

Back to Top ↑