Synthesis and Characterization of Cerium Molybdate Nanocontainers and Their Inhibitor Complexes

Published on January 25th, 2010 | By: pwray@ceramics.org

Volume 93 Issue 1, Pages 65 – 73

 

Ioannis A. Kartsonakis, George Kordas
Published Online: Oct 29 2009 4:19PM
DOI: 10.1111/j.1551-2916.2009.03310.x

 

ABSTRACT

Cerium molybdate nanocontainers were synthesized using a two-step process and then loaded with 8-hydroxyquinoline (8-HQ) or with 1-H-benzotriazole-4-sulfonic acid (1-BSA). First, polystyrene (PS) nanospheres were produced using emulsion polymerization. Second, the PS spheres were coated via the sol-gel method to form a cerium molybdate layer. Finally, the nanocontainers were made by calcination of cerium molybdate coated PS nanospheres. The products were characterized by scanning electron microscopy (SEM/EDX), transmission electron microscopy, FT-infrared (FT-IR) spectroscopy, X-ray diffraction, thermogravimetric analysis (TGA), and differential thermal analysis. Moreover, nanocontainers were loaded with 8-HQ or with 1-BSA and their presence was confirmed with FT-IR. The loading of the inhibitors in the nanocontainers was estimated with TGA. The loading amount of 8-HQ was 5.22% w/w and that of 1-BSA was 16.43%. Based on the size of the nanocontainers and the assumption that they are not broken, we deduced to the amount of approximately with 1.07 × 106 molecules of 8-HQ and 2.35 × 106 molecules of 1-BSA per nanocontainer. Furthermore, release of 8-HQ or 1-BSA in corrosive environment was studied by potentiodynamic measurements for aluminum alloys 2024-T3 (AA2024-T3) and DC01 carbon steel (DC01-CS) samples, showing that the inhibitors are released from the nanocontainers, suppressing the corrosion activities. SEM photographs confirmed that the nanocontainers maintained their shape after suspension in 0.5M NaCl solution for more than 72 h. Moreover, release of 8-HQ or 1-BSA in water was studied using spectrophotometer.

 

Online Access to Journal of the American Ceramic Society


Back to Previous Page
« « Previous Post     |    Next Post » »





Comments are closed.

Back to Top ↑